| Customization: | Available |
|---|---|
| Classification: | High-Alumina |
| Feature: | Long Time Materials |
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
| Payment methods: |
|
|---|---|
| Support payment in USD |
| Secure payments: | Every payment you make at Made-in-china.com is protected by the platform. |
|---|
| Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
|---|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
High alumina bricks are mainly made of clinker of bauxite and other materials, mixed at high temperature, formed, dried and sintered. The Al2O3 content of high alumina bricks varies according to different ratios. The general content is stable at 48%-80%, the maximum alumina content can reach 90%, and the refractory temperature can reach 1770ºC.
| International code name | SK35 | SK36 | SK37 | SK38 | SK40 |
| Al2O3/% | ≥48 | ≥55 | ≥65 | ≥75 | ≥80 |
| Fe2O3/% | ≤2 | ≤2 | ≤2 | ≤2 | ≤2 |
| Refractoriness | ≥1750 °C | ≥1770 °C | ≥1790 °C | ≥1790 °C | ≥1790 °C |
| Apparent porosity | ≤22% | ≤22% | ≤23% | ≤23% | ≤21% |
| Cold crushing strength | ≥39Mpa | ≥44Mpa | ≥49Mpa | ≥54Mpa | ≥65Mpa |
| Refractoriness under load (0.2MPa) | ≥1420 °C | ≥1470°C | ≥1500 °C | ≥1520 °C | ≥1530 °C |
| Reheating Linear Change (1500°C 2h) % | +0.1~ -0.4 *1450°C |
+0.1~ -0.4 | +0.1~ -0.4 | +0.1~ -0.4 |
+0.1~ -0.4 |